SHUNAN Wall Putty Based On White Cement

SHUNAN Wall Putty Based On White Cement
Product Detailed
putty1)Resistance of fungus and algae 2)Good match with substrate and finish coating 3)Good water vapour transmission ability

SHUNAN Cement Interior Wall Putty  and Water-resistant Exterior Wall Putty

1) It's a one component, preblended, cementitious outdoor wall plaster which, when mixed with water, is used prior to the application of finish coating.

2) Durable fillers,fill cracks and splits on interior/exterior surfaces

3) World class product of its kind, based on quality conch white cement. It is having water proof properties for use on cement plastered as well as on concrete walls and ceilings for both interior and exterior. Due to its unique qualities it enhances the life of paints and coating

Product Information

Packaging

    

      

· Weight: 25 kg

· Color: white

· Consumption: 1.5 ~2 kg/m2

· Shelf life & storage: 6 months after manufacturing date in dry ventilated place

· National Standard: JG/T157-2009

Product advantages

· Easy to use, just mix it with water

· Excellent weather resistance

· Good application ability, easy to apply and polish

· Good water-resistant and water vapour transmission ability

· High adhesive strength

· Good match with substrate and finish coating

· ISO9001 quality management system

· Green building material certificate

Field of application

· Suitable substrates: cement mortar, concrete

· Exterior for building 

Range of application:

 To be used for preparation of concrete, cement-lime and brick substrate before finishing.  May be used for filling small cavities, cracks and voids up to 5 mm deep.  After drying up, building façade may be painted. May be  used for inside finishing as well, including in humid areas (bathrooms, saunas, kitchens, etc.)High adhesion, durability and plasticity, good grindability and general workability

Limits of use

· Not suitable to use on oil substrate

· Not suitable to shrinkable substrate

Consumption

1.5~2 kg/m2

 Water addition: 1kg/ 0.33 lt

Product specification

Tools:

Elec-mixer, Bucket, Trowel

Substrate requirement

The substrate should be sound, dry, flat, clean and durable

Substrate preparation

· Clean the substrate until free from dust, oil, or any other stains

· When high temperature season or dry substrate, substrate should be wet one day before

Application

                            

· Put 8.25 liters clean water in a bucket. Gradually add one bag (25 kg) of powder into water

· Mix properly until homogeneous and lump-free

· Leave the product for 5~10 minutes. Then mix the second time for 1~2 minutes

· Apply the 1st coat of product onto the substrate. When the finish is dry, apply the 2nd coat.   Each thickness is about 0.5 ~0.6 mm

· Ensure a flat, smooth and pinhole free coating

· Normally, after 24 hours (depend on weather and substrate), polish the surface

  After that, apply the finish coating

 Application environment

· Temperature: 5°C~35°C

· Avoid rain, high temperature and frost

· Avoid direct sunlight or strong wind

 Safety

· May cause serious damage to eyes

· May be sensitive to skin in case of contact. lrritable for eyes, respiratory system and skin

· Keep out of the reach of children

· Avoid breathing the dust

· In case of contact with eyes,rinse eyes immediately with plenty of water and consult a doctor

· Wear suitable protective clothing,gloves and eye/face protection